Characteristics of Hybrid Composite with Graphite as Filler
Abstract
Trial study is completed on the impact of graphite fillers on mechanical properties of jute and E-glass fiber fortified epoxy cross breed composite.Composites were readied utilizing hand layup technique with weight rate of graphite as filler material differing from 0%,2.5%,5% and 7.5% with 3 layers of jute fiber and 4 layers of E-glass fiber as support.The resultsshowed that the mechanical properties of the composites predominantly rely on upon scattering state of the filler particles, molecule size and total structure. Significant change in bowing quality of the composite after expanding the filler substance was watched and the ductile property is additionally expanded.
References
Agarwal D.Broutman J. Fiber Composites. Prague: SNTL. 1987; 294p.
D. D. Rodrigues, J. G. Broughton. Silane surface
modification of boron carbide in epoxy composites. International Journal of Adhesion &Adhesives. 2013; 46: 62–73p.
D. I. Tee, M. Mariatti, A. Azizan, C. H. See, K. F. Chong. Effect of silane-based coupling agent on the properties of silver nanoparticles filled epoxy composites. Composites Science and Technology.2010; 67(11-12): 2584–2591p.
G. Shi, M. Q. Zhang, M. Z. Rong, B. Wetzel, K. Friedrich. Sliding wear behaviour of epoxy containing nano-Al2O3 particles with different pre-treatments.Wear. 2004; 256(11-12): 1072–1081p.
J. Abenojar, M. A. Martínez, F. Velasco, V. Pascual-Sánchez, J. M. Martín-Martinez. Effect of boron carbide filler on the curing and mechanical properties ofan epoxy resin.Journal of Adhesion. 2009;85(4-5): 216–238p.
Kim B.C., Park S.W., Lee D.G. Fracture toughness of the nano-particle reinforced epoxy composite. Composite Structures. 2008; 86: 69-77p.
Kumar V., Tyagi L., Sinha S. Wood flour-reinforced plastic composites: A review. Reviews in Chemical Engineering. 2015; 27(5-6): 253-264p.
Refbacks
- There are currently no refbacks.